Publicación:
CHARACTERIZATION NANOMECHANICS OF WOOD CELL STRUCTURE AND ANATOMY IN EUCALYPTUS NITENS AND ITS RELATION TO THE CRACKING AND FRACTURES IN ROUND WOOD

dc.creatorWILLIAM ARNOLDO GACITÚA ESCOBAR
dc.creatorCECILIA DEL CARMEN BUSTOS ÁVILA
dc.date2012
dc.date.accessioned2025-01-10T14:33:40Z
dc.date.available2025-01-10T14:33:40Z
dc.date.issued2012
dc.description.abstractTHE AIM OF THIS STUDY WAS TO DENE THE MINIMUM VOLUMEN IN TREES OF E. NITENS THAT CHARACTERIZE THE MECHANICAL AND ANATOMY BEHAVIOR FOR NON-DESTRUCTIVE SAMPLING. E TREES WERE CUT FROM SITES LOCATED IN MULCHEN AND YUNGAY IN THE REGION OF BÍO BÍO. RELATIONSHIPS WERE FOUND BETWEEN NANO-MECHANICAL PROPERTIES, WOOD ANATOMY AND WOOD CRACKS AND FRACTURES. E RESPONSE VARIABLES WERE THE DUCTILITY RATIO (E/H) AND THE MODULUS OF RESILIENCE (UR), IN THE S2 LAYER AND MIDDLE LAMELLA. E RESULTS SHOWED THAT THE REPRESENTATIVE VOLUME, FROM E. NITENS FAMILIES IS AT 3 METER HIGH FROM BASE OF THE TREES AND BETWEEN THE 5TH TO 7TH ANNUAL RINGS. ALSO, IT WAS ESTABLISHED THAT THE MIDDLE LAMELLA IS MORE BRITTLE THAN THE S2 LAYER. RELATIONSHIP BETWEEN THE VESSELS MORPHOLOGY AND THE LEVEL OF THE WOOD CRACKING WAS OBSERVED. A HIGH AREA OF VESSELS, A HIGH VESSEL DIAMETER AND A SMALL FREQUENCY OF THEM, RESULTED IN HIGH CRACKING. E CRACKS WERE MAINLY CONCENTRATED IN THERST METERS OF TREE, WERE WE FOUND A GOOD RELATIONSHIP OF THIS RESPONSE VARIABLE WITH THE E/H RATIO FOR THE MIDDLE LAMELLA; THERE WAS A SIGNICANT CHANGE OF THIS RATIO AT 3 METERS HIGH. CRACKS WERE EVIDENT ON EARLYWOOD AND FROM
dc.formatapplication/pdf
dc.identifier.doi10.4067/S0718-221X2012005000007
dc.identifier.issn0717-3644
dc.identifier.issn0718-221X
dc.identifier.urihttps://repositorio.ubiobio.cl/handle/123456789/7963
dc.languagespa
dc.publisherMADERAS: CIENCIA Y TECNOLOGIA
dc.relation.uri10.4067/S0718-221X2012005000007
dc.rightsPUBLICADA
dc.subjectWOOD ULTRASTRUCTURE
dc.subjectWOOD ANATOMY
dc.subjectNANOMECHANICAL PROPERTIES
dc.subjectNANOINDENTATIONS
dc.subjectCRACKS
dc.subjectULTRAESTRUC-TURA DE LA MADERA
dc.subjectPROPIEDADES MECÁNICAS
dc.subjectNANOINDENTACIONES
dc.subjectFRACTURAS.
dc.subjectANATOMÍA DE LA MADERA
dc.titleCHARACTERIZATION NANOMECHANICS OF WOOD CELL STRUCTURE AND ANATOMY IN EUCALYPTUS NITENS AND ITS RELATION TO THE CRACKING AND FRACTURES IN ROUND WOOD
dc.title.alternativeCARACTERIZACIÓN NANOMECÁNICA DE LA ESTRUCTURA CELULAR Y ANATÓMICA DE EUCALYPTUS NITENS Y SU RELACIÓN CON LA FRECUENCIA DE GRIETAS Y RAJADURAS EN MADERA REDONDA
dc.typeARTÍCULO
dspace.entity.typePublication
ubb.EstadoPUBLICADA
ubb.Otra ReparticionDEPARTAMENTO DE INGENIERIA EN MADERAS
ubb.Otra ReparticionDEPARTAMENTO DE INGENIERIA EN MADERAS
ubb.SedeCONCEPCIÓN
ubb.SedeCONCEPCIÓN