FRACTURE IN EUCALYPTUS NITENS WOOD: EFFECT OF NANOMECHANICAL PROPERTIES, ULTRASTRUCTURE AND ANATOMICAL LEVEL

Vista sencilla de ítem
dc.creatorWILLIAM ARNOLDO GACITÚA ESCOBAR
dc.creatorCECILIA DEL CARMEN BUSTOS ÁVILA
dc.date2012
dc.date.accessioned2025-01-10T14:40:25Z
dc.date.available2025-01-10T14:40:25Z
dc.date.issued2012
dc.description.abstractTHIS STUDY WAS CONDUCTED TO INVESTIGATE THE CAUSES AND POSIBLES FACTORS RELATED TO FRACTURES IN THE CELLULAR STRUCTURE IN EUCALYPTUS NITENS. NANOMECHANICAL CELL WALL PROPERTIES AT THE MIDDLE LAMELLA LEVEL (ML), S1 AND S2 LAYERS WERE EVALUATED. IN ADDITION, THE AREA, AND DIAMETER OF VESSELS WERE MEASURED. THESE PARAMETERS WERE ASSOCIATED WITH EXTREME LEVELS OF CRACKING (HIGH AND LOW) IN TWO EUCALYPTUS NITENS FAMILIES. THE SAMPLES WERE TAKED FROM TWO SITES OF THE 8TH REGION OF CHILE. THE ANALYSIS OF THE DUCTILITY RATIO (E/H) DEMONSTRATED THAT THE ML IS MORE BRITTLE THAN THE S1 LAYER; AND THE S1 IS MORE BRITTLE THAN S2 LAYER. THE ML AND S1 LAYER BEHAVE LIKE RESILIENT MATERIALS, BUT NOT THE S2 LAYER. THE DIFFERENCE IN THE MODULUS OF RESILIENCE WAS RELATED TO HIGHER SHEAR STRESSES AT THE ML/S2 AND AT S1/S2 INTERFACES. THE CHARACTERIZATION OF THE VESSELS SHOWED THAT THE FAMILIES WITH GREATER LEVEL OF CRACKING HAVE ALSO LOWER FREQUENCY AND GREATER AREA AND DIAMETER OF VESSELS THE S1 LAYER WAS WEAKER TAN S2 LAYER AND LM DUE TO THEIR DIFFERENCE IN RESISTANCE BETWEEN THEM AND COMBINED WITH THE INTERNAL STRESSES MIGHT PROPAGATE THE MICROCRACKS.
dc.formatapplication/pdf
dc.identifier.doi10.4067/S0718-221X2012000200009
dc.identifier.issn0717-3644
dc.identifier.issn0718-221X
dc.identifier.urihttps://repositorio.ubiobio.cl/handle/123456789/8462
dc.languagespa
dc.publisherMADERAS: CIENCIA Y TECNOLOGIA
dc.relation.uri10.4067/S0718-221X2012000200009
dc.rightsPUBLICADA
dc.titleFRACTURE IN EUCALYPTUS NITENS WOOD: EFFECT OF NANOMECHANICAL PROPERTIES, ULTRASTRUCTURE AND ANATOMICAL LEVEL
dc.title.alternativeFRACTURAS EN MADERA DE EUCALYPTUS NITENS: EFECTO DE LAS PROPIEDADES MECÁNICAS A NIVEL ULTRAESTRUCTURAL Y DE LA ANATOMÍA CELULAR
dc.typeARTÍCULO
dspace.entity.typePublication
ubb.EstadoPUBLICADA
ubb.Otra ReparticionDEPARTAMENTO DE INGENIERIA EN MADERAS
ubb.Otra ReparticionDEPARTAMENTO DE INGENIERIA EN MADERAS
ubb.SedeCONCEPCIÓN
ubb.SedeCONCEPCIÓN
Archivos
Colecciones
Artículos científicos